Semiconductor transistors with contact holes close to gates

ABSTRACT

A structure and a method for forming the same. The structure includes (a) a semiconductor layer including a channel region disposed between first and second S/D regions; (b) a gate dielectric region on the channel region; (c) a gate region on the gate dielectric region and electrically insulated from the channel region by the gate dielectric region; (d) a protection umbrella region on the gate region, wherein the protection umbrella region comprises a first dielectric material, and wherein the gate region is completely in a shadow of the protection umbrella region; and (e) a filled contact hole (i) directly above and electrically connected to the second S/D region and (ii) aligned with an edge of the protection umbrella region, wherein the contact hole is physically isolated from the gate region by an inter-level dielectric (ILD) layer which comprises a second dielectric material different from the first dielectric material.

BACKGROUND OF THE INVENTION

1. Technical Field

The present invention relates to semiconductor FETs (field effect transistors), and more specifically, to FETs with contact holes close to gates.

2. Related Art

During the fabrication of a typical FET (field effect transistor), after gate and source/drain (S/D) regions of the typical FET device are formed, a dielectric layer is deposited on top of the entire FET. Next, S/D contact holes are created in the dielectric layer and then filled with an electrically conducting material so as to provide electrical access to the S/D regions of the FET. As a result, to increase device density, there is a need for a transistor structure (and a method for forming the same) in which S/D contact holes are formed close to but electrically insulated from the gate of the transistor structure.

SUMMARY OF THE INVENTION

The present invention provides a structure formation method, comprising providing a structure including (a) a semiconductor layer including (i) a channel region and (ii) first and second source/drain (S/D) regions, wherein the channel region is disposed between and electrically coupled to the first and second S/D regions, (b) a gate dielectric region in direction physical contact with the channel region via an interfacing surface which defines a reference direction perpendicular to the interfacing surface, wherein the gate dielectric region is above the channel region in the reference direction, (c) a gate region in direct physical contact with the gate dielectric region, wherein the gate dielectric region is sandwiched between and electrically insulates the gate region and the channel region, and (d) a hard cap region on the gate region; forming a protection umbrella region from the hard cap region such that the gate region is completely in a shadow of the protection umbrella region, wherein the shadow of the protection umbrella region comprises a space shielded by the protection umbrella region from an imaginary light point source (i) directly above the protection umbrella region in the reference direction and (ii) infinitely far from the protection umbrella region; blanket depositing an inter-level dielectric (ILD) layer on the structure after said forming the protection umbrella region is performed; creating a contact hole in the ILD layer directly above the second S/D region and aligned with an edge of the protection umbrella region, wherein the contact hole is physically isolated from the gate region by the ILD layer; and filling the contact hole with an electrically conducting material.

The present invention also provides a structure formation method, comprising providing a structure including (a) a semiconductor layer including (i) a channel region and (ii) first and second source/drain (S/D) regions, wherein the channel region is disposed between and electrically coupled to the first and second S/D regions, (b) a gate dielectric region in direction physical contact with the channel region via an interfacing surface which defines a reference direction perpendicular to the interfacing surface, wherein the gate dielectric region is above the channel region in the reference direction, (c) a gate region in direct physical contact with the gate dielectric region, wherein the gate dielectric region is sandwiched between and electrically insulates the gate region and the channel region, and wherein the gate region comprises (i) a polysilicon region on and in direct physical contact with the gate dielectric region and (ii) first and second gate silicide regions on first and second sidewalls of the polysilicon region, respectively; (d) a hard cap region on the gate region; forming a protection umbrella region from the hard cap region such that the gate region is completely in a shadow of the protection umbrella region, wherein the shadow of the protection umbrella region comprises a space shielded by the protection umbrella region from an imaginary light point source (i) directly above the protection umbrella region in the reference direction and (ii) infinitely far from the protection umbrella region; blanket depositing an inter-level dielectric (ILD) layer on the structure after said forming the protection umbrella region is performed; creating a contact hole in the ILD layer directly above the second S/D region and aligned with an edge of the protection umbrella region, wherein the contact hole is physically isolated from the gate region by the ILD layer, and wherein said creating the contact hole comprises (i) forming an oxide layer on the ILD layer, (ii) creating an opening in the oxide layer, and, (ii) etching the ILD layer through the opening using the oxide layer and the protection umbrella region as a blocking mask; and filling the contact hole with an electrically conducting material.

The present invention also provides a structure, comprising (a) a semiconductor layer including (i) a channel region and (ii) first and second source/drain (S/D) regions, wherein the channel region is disposed between and electrically coupled to the first and second S/D regions; (b) a gate dielectric region in direction physical contact with the channel region via an interfacing surface which defines a reference direction perpendicular to the interfacing surface, wherein the gate dielectric region is above the channel region in the reference direction; (c) a gate region in direct physical contact with the gate dielectric region, wherein the gate dielectric region is sandwiched between and electrically insulates the gate region and the channel region; (d) a protection umbrella region on the gate region, wherein the protection umbrella region comprises a first dielectric material, and wherein the gate region is completely in a shadow of the protection umbrella region, wherein the shadow of the protection umbrella region comprises a space shielded by the protection umbrella region from an imaginary light point source (i) directly above the protection umbrella region in the reference direction and (ii) infinitely far from the protection umbrella region; and (e) a filled contact hole (i) directly above and electrically connected to the second S/D region and (ii) aligned with an edge of the protection umbrella region, wherein the contact hole is physically isolated from the gate region by an inter-level dielectric (ILD) layer, and wherein the ILD layer comprises a second dielectric material different from the first dielectric material.

The present invention provides a transistor structure (and a method for forming the same) in which S/D contact holes are formed close to but electrically insulated from the gate of the transistor structure.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-1I illustrate the fabrication steps for forming a first FET, in accordance with embodiments of the present invention.

FIGS. 2A-2F illustrate the fabrication steps for forming a second FET in accordance with embodiments of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

FIGS. 1A-1I illustrate the fabrication steps for forming a first FET 100, in accordance with embodiments of the present invention. More specifically, with reference to FIG. 1A, in one embodiment, the fabrication steps for forming the first FET 100 starts out with a semiconductor (e.g., silicon, germanium, etc.) substrate 110.

Next, in one embodiment, a gate dielectric layer 120 is formed on top of the Si substrate 110. Illustratively, the gate dielectric layer 120 comprises silicon dioxide (SiO₂) and is formed by oxidation of a top surface 119 of the Si substrate 110.

Next, in one embodiment, a gate layer 130 is formed on top of the gate dielectric layer 120. Illustratively, the gate layer 130 comprises polysilicon and is formed by chemical vapor deposition (CVD) of polysilicon on top of the gate dielectric layer 120.

Next, in one embodiment, an oxide hard mask layer 140 is formed on top of the polysilicon gate layer 130 by, illustratively, CVD of SiO2.

Next, in one embodiment, a patterned photoresist layer 150 is formed on top of the oxide hard mask layer 140 such that regions of the oxide hard mask layer 140 to be later removed are not covered by the patterned photoresist layer 150 while regions of the oxide hard mask layer 140 to remain are covered by the patterned photoresist layer 150. In one embodiment, the patterned photoresist layer 150 is formed using any conventional lithographic process.

Next, in one embodiment, the patterned photoresist layer 150 is used as a blocking mask for a directional etching of (i) the oxide hard mask layer 140 and then (ii) the polysilicon gate layer 130. In one embodiment, the directional selective (i.e., using a blocking mask) etching of the polysilicon gate layer 130 is only partial (i.e., not completely through the polysilicon gate layer 130). The directional etching of the oxide hard mask layer 140 results in a patterned oxide hard cap 140′ (FIG. 1B). Next, the patterned photoresist layer 150 is removed resulting in the structure 100 of FIG. 1B.

Next, in one embodiment, with reference to FIG. 1C, gate silicide spacers 160 a and 160 b are formed on sidewalls 132 a and 132 b of the polysilicon gate layer 130, respectively. Illustratively, the gate silicide spacers 160 a and 160 b comprise a metal silicide (such as tungsten silicide) and are formed by first (i) blanket depositing a conformal layer of tungsten silicide (not shown) on top of the structure 100 of FIG. 1B and then (ii) directionally etching the deposited tungsten silicide layer leaving the gate silicide spacers 160 a and 160 b on sidewalls 132 a and 132 b of the polysilicon gate layer 130, respectively, while removing the silicide from horizontal surfaces. In one embodiment, the step (ii) is performed such that sidewalls 142 a and 142 b of the oxide hard cap 140′ are not covered by the silicide spacers 160 a and 160 b, respectively.

In the embodiments described above, the gate spacers 160 a and 160 b comprise tungsten silicide and are formed by blanket deposition of tungsten silicide followed by directional etching of the deposited tungsten silicide. In an alternative embodiment, the gate spacers 160 a and 160 b can comprise a metal and are formed by blanket deposition of the metal followed by directional etching of the deposited metal. In yet another alternative embodiment, the gate spacers 160 a and 160 b can comprise tungsten silicide (as described above) but are formed by (a) blanket deposition of tungsten on top of the structure 100 of FIG. 1B, (b) then heating the structure 100 to cause the deposited tungsten to chemically react with silicon to form tungsten silicide, then (c) removing unreacted tungsten, and then (d) directionally etching the formed tungsten silicide to remove tungsten silicide from horizontal surfaces leaving only the tungsten silicide gate spacers 160 a and 160 b on the sidewalls 132 a and 132 b of the polysilicon gate layer 130, respectively.

Next, with reference to FIG. 1D, in one embodiment, the gate silicide spacers 160 a and 160 b and the oxide hard cap 140′ are used as a blocking mask for a directional etching of the polysilicon gate layer 130 stopping at the gate dielectric layer 120. As a result, what remains of the polysilicon gate layer 130 is a polysilicon gate region 130′. The combination of the polysilicon gate region 130′, the oxide hard cap 140′, and the gate suicide spacers 160 a and 160 b can be referred to as a gate stack 130′,140′,160 a,160 b, whereas the combination of the polysilicon gate region 130′ and the gate suicide spacers 160 a and 160 b can be referred to as the gate region 130′,160 a,160 b.

Next, in one embodiment, the gate stack 130′,140′,160 a,160 b is used as a blocking mask for forming source/drain (S/D) extension regions 111 a and 11 b, and halo regions (not shown for simplicity) in the Si substrate 110 on opposing sides of the gate stack 130′,140′,160 a,160 b. The formation of the S/D extension regions 111 a and 111 b and the halo regions can be by ion implantation.

Next, with reference to FIG. 1E, in one embodiment, nitride spacers 170 a and 170 b are formed on sidewalls of the gate stack 130′,140′,160 a,160 b. Illustratively, the nitride spacers 170 a and 170 b are formed by (a) depositing a nitride spacer layer (not shown) on the entire structure 100 of FIG. 1D, and then (b) directionally etching the deposited nitride spacer layer resulting in the nitride spacers 170 a and 170 b on sidewalls of the gate stack 130′,140′,160 a,160 b. Said directional etching of the deposited nitride spacer layer typically also removes portions of gate dielectric layer 120 not masked by gate stack 130′,140′,160 a,160 b and nitride spacers 170 a and 170 b.

Next, in one embodiment, the nitride spacers 170 a and 170 b and the gate stack 130′,140′,160 a,160 b are used as a blocking mask for forming S/D regions 112 a and 112 b in the Si substrate 110 on opposing sides of the gate stack 130′,140′,160 a,160 b. The formation of the S/D regions 112 a and 112 b can be by ion implantation followed by an anneal step.

The S/D extension region 111 a and the S/D region 112 a can be referred to as the S/D block 111 a,112 a. Similarly, the S/D extension region 111 b and the S/D region 112 b can be referred to as the S/D block 111 b,112 b. The S/D blocks 111 a,112 a and 111 b,112 b define a channel region 113 disposed between the S/D blocks 111 a,112 a and 111 b,112 b directly under the gate dielectric layer 120. The resulting structure 100 is depicted in FIG. 1E.

Next, with reference to FIG. 1F, in one embodiment, a protection umbrella region 140″ is created from the oxide hard cap 140′ such that the gate region 130′,160 a,160 b is completely in a shadow of the protection umbrella region 140″. Here, the shadow of the protection umbrella region 140″ is defined to be a space shielded by the protection umbrella region 140″ from an imaginary light point source (not shown) directly above and infinitely far from the protection umbrella region 140″.

In one embodiment, the protection umbrella region 140″ is formed by selectively depositing silicon dioxide only on the oxide hard cap 140′ so as to enlarge the oxide hard cap 140′. The enlargement of the oxide hard cap 140′ is continued until the gate silicide spacers 160 a and 160 b are completely in a shadow of the resulting protection umbrella region 140″. In one embodiment, said selectively depositing silicon dioxide only on the oxide hard cap 140′ involves (i) submerging the structure 100 of FIG. 1F in a solution of H₂SiF₆ (hexafluoro silicic acid) in H₂ 0, and then (ii) causing the solution to become over-saturated (by increasing the temperature of the solution in one embodiment) so as to create SiO2 that deposits on the oxide hard cap 140′ resulting in the protection umbrella region 140″. The chemical reaction that results from the over-saturation of the solution of H₂SiF₆ in H₂ 0 is as follows. H₂SiF₆+2H₂ 0-->6HF+SiO₂

It should be noted that the created SiO₂ deposits only on surfaces that have active hydroxyl groups “OH”. As a result, the created SiO₂ deposits only on the SiO₂ surfaces of the oxide hard cap 140′ (which have active hydroxyl groups) and not on silicide or nitride surfaces (which do not have active hydroxyl groups) of the regions 160 a, 160 b, 114 a, 114 b, 170 a, and 170 b. In one embodiment, the liquid-phase deposition of SiO₂ on only the SiO₂ surface to form protection umbrella region 140″ described above can be carried out in conditions and equipment specified in U.S. Pat. No. 6,251,753, U.S. Pat. No. 5,232,781, and U.S. Pat. No. 6,653,245, which are hereby incorporated in this specification of the present invention.

Next, in one embodiment, S/D silicide regions 114 a and 114 b are formed on top of the S/D regions 112 a and 112 b, respectively, using any conventional process.

Next, with reference to FIG. 1G, in one embodiment, an inter-level dielectric (ILD) layer 180, comprising a low-K (i.e., K<3.5, wherein K is the dielectric constant) material in one embodiment, is formed on top of the structure 100 of FIG. 1F by, illustratively, a CVD or spin-on process. Next, in one embodiment, the low-K dielectric layer 180 is planarized until a top surface 144 of the protection umbrella region 140″ is exposed to the surrounding ambient.

Next, with reference to FIG. 1H, in one embodiment, an oxide layer 190 is formed on top of the entire structure 100 of FIG. 1F. Next, an opening 191 is created in the oxide layer 190 by, illustratively, a conventional lithographic process. The creation of the opening 191 in the oxide layer 190 may result in an indentation 192 in the protection umbrella region 140″ due to over-etching. In one embodiment, the indentation 192 is shallow such that no electrically conducting region of the gate stack 130′,140′,160 a,160 b is exposed to the surrounding ambient.

Next, with reference to FIG. 1I, in one embodiment, the oxide layer 190 and the protection umbrella region 140″ are used as a blocking mask for a directional etching of the low-K dielectric layer 180 so as to create a contact hole 197 in the low-K dielectric layer 180 such that the S/D silicide region 114 b is exposed to the surrounding ambient through the contact hole 197. In one embodiment, the relative position of the opening 191 in the oxide layer 190 with respect to the silicide spacer 160 b is such that the contact hole 197 is formed aligned with an edge 143 of the protection umbrella region 140″. Next, in one embodiment, the contact hole 197 is filled with an electrically conducting material (tungsten (W) in one embodiment) so as to provide electrical access to the S/D region 112 b.

It should be noted that, because the gate region 130′,160 a,160 b is completely in a shadow of the protection umbrella region 140″, the silicide spacer 160 b is not exposed to the surrounding ambient when the contact hole 197 is created in the low-K dielectric layer 180. As a result, the W-filled contact hole 197 is electrically insulated from the gate region 130′,160 a,160 b (comprising regions 130′, 160 a, and 160 b) by the low-K dielectric layer 180.

FIGS. 2A-2F illustrate the fabrication steps for forming a second FET 200, in accordance with embodiments of the present invention. More specifically, with reference to FIG. 2A, in one embodiment, the fabrication steps for forming the second FET 200 starts out with a structure similar to the structure 100 of FIG. 1A. For simplicity, all reference numerals herein have three numeric digits starting with the numeric figure number. In addition, similar regions have the identical reference numerals except for the first digit which is used to indicate the numeric figure number. For example, the substrate 110 (FIG. 1A) and the substrate 210 (FIG. 2A) are similar.

Next, in one embodiment, the patterned photoresist layer 250 is used as a blocking mask for a directional etching of (i) the oxide hard mask layer 240 and then (ii) the polysilicon gate layer 230 stopping at the gate dielectric layer 220. The directional selective (i.e., using a blocking mask) etching of the oxide hard mask layer 240 and the polysilicon gate layer 230 results in an oxide hard cap 240′ and a polysilicon gate region 230′ (FIG. 2B). Next, the patterned photoresist layer 250 is removed resulting in the structure 200 of FIG. 2B. With reference to FIG. 2B, the oxide hard cap 240′ and the polysilicon gate region 230′ can be referred to as a gate stack 230′,240′.

Next, in one embodiment, the gate stack 230′,240′ is used as a blocking mask for forming source/drain (S/D) extension regions 211 a and 211 b and halo regions (not shown for simplicity) in the Si substrate 210 on opposing sides of the gate stack 230′,240′. The formation of the S/D extension regions 211 a and 211 b and halo regions can be by ion implantation.

Next, with reference to FIG. 2C, in one embodiment, nitride spacers 270 a and 270 b are formed on sidewalls 242 a and 242 b of the polysilicon gate region 230′, respectively. Illustratively, the nitride spacers 270 a and 270 b are formed by (a) depositing a nitride spacer layer (not shown) on the entire structure 200 of FIG. 2B, and then (b) directionally etching the deposited nitride spacer layer resulting in the nitride spacers 270 a and 270 b. In one embodiment, said directionally etching of the deposited nitride spacer layer is performed such that sidewall portions 242 a′ and 242 b′ of the sidewalls 242 a and 242 b, respectively, of the polysilicon gate region 230′ are exposed to the surrounding ambient (i.e., not covered by the nitride spacers 270 a and 270 b). Said directional etching of the deposited nitride spacer layer typically also removes portions of gate dielectric layer 220 not masked by gate stack 230′,240′,260 a,260 b and nitride spacers 270 a and 270 b.

Next, the nitride spacers 270 a and 270 b and the gate stack 230′,240′ are used as a blocking mask for forming S/D regions 212 a and 212 b in the Si substrate 210 on opposing sides of the gate stack 230′,240′. The formation of the S/D regions 212 a and 212 b can be by ion implantation followed by an anneal process.

The S/D extension region 21 la and the S/D region 212 a can be referred to as the S/D block 211 a,212 a. Similarly, the S/D extension region 211 b and the S/D region 212 b can be referred to as the S/D block 211 b,212 b. The S/D blocks 211 a,212 a and 211 b,212 b define a channel region 113 disposed between the S/D blocks 211 a,212 a and 211 b,212 b directly under the gate dielectric layer 120.

Next, with reference to FIG. 2D, in one embodiment, gate silicide regions 260 a and 260 b are formed on exposed-to-ambient sidewall portions 242 a′ and 242 b′ (FIG. 2C) of the polysilicon gate region 230′, respectively, while S/D silicide regions 214 a and 214 b are formed on the S/D regions 212 a and 212 b, respectively. In one embodiment, the gate silicide regions 260 a and 260 b and the S/D silicide regions 214 a and 214 b are formed by (i) depositing a metal layer (not shown) on top of the entire structure 200 of FIG. 2C, and then (ii) annealing (heating) the structure 200 at a high temperature so as to cause the metal of the deposited metal layer to chemically react with silicon to form the gate silicide regions 260 a and 260 b and the S/D silicide regions 214 a and 214 b. Finally, unreacted metal of the deposited metal layer is removed by, illustratively, a wet etch step, resulting in the structure 200 of FIG. 2D. The combination of the polysilicon gate region 230′ and the gate silicide spacers 260 a and 260 b can be referred to as the gate region 230′,260 a,260 b.

Next, with reference to FIG. 2E, in one embodiment, a protection umbrella region 240″ is created from the oxide hard cap 240′ such that the gate region 230′,260 a,260 b is completely in a shadow of the protection umbrella region 240″. In one embodiment, the formation of the protection umbrella region 240″ is similar to the formation of the protection umbrella region 140″ of FIG. 1F.

Next, in one embodiment, an ILD layer 280, comprising a low-K (i.e., K<3.5, wherein K is the dielectric constant) material in one embodiment, is formed on top of the structure 200 by, illustratively, a CVD or spin-on process. Next, in one embodiment, the low-K dielectric layer 280 is planarized until a top surface 244 of the protection umbrella region 240″ is exposed to the surrounding ambient.

Next, with reference to FIG. 2F, in one embodiment, an oxide layer 290 is formed on top of the entire structure 200 of FIG. 2E. Next, a metal-filled contact hole 297 similar to the W-filled contact hole 197 of FIG. 1I is formed in the oxide layer 290 and the low-K dielectric layer 280. In one embodiment, the metal-filled contact hole 297 comprises tungsten (W) and the formation of the W-filled contact hole 297 is similar to the formation of the W-filled contact hole 197 of FIG. 1I.

It should be noted that, because the gate region 230′,260 a,260 b is completely in a shadow of the protection umbrella region 240″, the gate silicide spacer 260 b is not exposed to the surrounding ambient when the contact hole 297 is created in the oxide layer 290 and the low-K dielectric layer 280. As a result, the W-filled contact hole 297 is electrically insulated from the gate region 230′,260 a,260 b by the low-K dielectric layer 280.

While particular embodiments of the present invention have been described herein for purposes of illustration, many modifications and changes will become apparent to those skilled in the art. Accordingly, the appended claims are intended to encompass all such modifications and changes as fall within the true spirit and scope of this invention. 

1. A structure formation method, comprising: providing a structure including: (a) a semiconductor layer including (i) a channel region and (ii) first and second source/drain (S/D) regions, wherein the channel region is disposed between and electrically coupled to the first and second S/D regions, (b) a gate dielectric region in direction physical contact with the channel region via an interfacing surface which defines a reference direction perpendicular to the interfacing surface, wherein the gate dielectric region is above the channel region in the reference direction, (c) a gate region in direct physical contact with the gate dielectric region, wherein the gate dielectric region is sandwiched between and electrically insulates the gate region and the channel region, and (d) a hard cap region on the gate region; forming a protection umbrella region from the hard cap region such that the gate region is completely in a shadow of the protection umbrella region, wherein the shadow of the protection umbrella region comprises a space shielded by the protection umbrella region from an imaginary light point source (i) directly above the protection umbrella region in the reference direction and (ii) infinitely far from the protection umbrella region; blanket depositing an inter-level dielectric (ILD) layer on the structure after said forming the protection umbrella region is performed; creating a contact hole in the ILD layer directly above the second S/D region and aligned with an edge of the protection umbrella region, wherein the contact hole is physically isolated from the gate region by the ILD layer; and filling the contact hole with an electrically conducting material.
 2. The method of claim 1, wherein the protection umbrella region comprises silicon dioxide, and wherein the ILD layer comprises a low-K dielectric material, wherein K<3.5.
 3. The method of claim 1, wherein the electrically conducting material comprises tungsten.
 4. The method of claim 1, wherein the gate region comprises (i) a polysilicon region on and in direct physical contact with the gate dielectric region and (ii) first and second gate silicide regions on first and second sidewalls of the polysilicon region, respectively.
 5. The method of claim 4, wherein the first and second gate silicide regions are not in direct physical contact with the gate dielectric region.
 6. The method of claim 4, wherein said providing the structure comprises: providing the semiconductor layer; forming a gate dielectric layer on the semiconductor layer; forming a polysilicon gate layer on the gate dielectric layer; forming a hard mask layer on the polysilicon gate layer; selectively etching the hard mask layer so as to form the hard cap region; partially etching the polysilicon gate layer using the hard cap region as a first blocking mask so as to form a polysilicon gate block from the polysilicon gate layer; forming the first and second gate silicide regions on sidewalls of the polysilicon gate block; and etching the polysilicon gate block stopping at the gate dielectric layer using the hard cap region and the first and second gate silicide regions as a second blocking mask so as to form the polysilicon region from the polysilicon gate block.
 7. The method of claim 4, wherein said providing the structure comprises: providing the semiconductor layer; forming a gate dielectric layer on the semiconductor layer; forming a polysilicon gate layer on the gate dielectric layer; forming a hard mask layer on the polysilicon gate layer; selectively etching the hard mask layer so as to form the hard cap region; etching the polysilicon gate layer stopping at the gate dielectric layer using the hard cap region as a blocking mask so as to form the polysilicon region from the polysilicon gate layer; forming first and second nitride regions on first and second sidewalls of the polysilicon region, respectively, such that first and second sidewall portions of the first and second sidewalls of the polysilicon gate block, respectively, are not covered by the first and second nitride regions, respectively; and forming the first and second silicide regions on the first and second sidewall portions, respectively.
 8. The method of claim 1, wherein said forming the protection umbrella region from the hard cap region comprises selectively depositing a dielectric material on only the hard cap region.
 9. The method of claim 8, wherein the hard cap region comprise silicon dioxide, and wherein the dielectric material comprises silicon dioxide.
 10. The method of claim 1, wherein said creating the contact hole comprises etching the ILD layer using a blocking mask including the protection umbrella region.
 11. The method of claim 10, wherein said etching the ILD layer comprises: forming an oxide layer on the ILD layer; creating an opening in the oxide layer; and etching the ILD layer through the opening using the oxide layer and the protection umbrella region as the blocking mask.
 12. A structure formation method, comprising: providing a structure including: (a) a semiconductor layer including (i) a channel region and (ii) first and second source/drain (S/D) regions, wherein the channel region is disposed between and electrically coupled to the first and second S/D regions, (b) a gate dielectric region in direction physical contact with the channel region via an interfacing surface which defines a reference direction perpendicular to the interfacing surface, wherein the gate dielectric region is above the channel region in the reference direction, (c) a gate region in direct physical contact with the gate dielectric region, wherein the gate dielectric region is sandwiched between and electrically insulates the gate region and the channel region, and wherein the gate region comprises (i) a polysilicon region on and in direct physical contact with the gate dielectric region and (ii) first and second gate silicide regions on first and second sidewalls of the polysilicon region, respectively; (d) a hard cap region on the gate region; forming a protection umbrella region from the hard cap region such that the gate region is completely in a shadow of the protection umbrella region, wherein the shadow of the protection umbrella region comprises a space shielded by the protection umbrella region from an imaginary light point source (i) directly above the protection umbrella region in the reference direction and (ii) infinitely far from the protection umbrella region; blanket depositing an inter-level dielectric (ILD) layer on the structure after said forming the protection umbrella region is performed; creating a contact hole in the ILD layer directly above the second S/D region and aligned with an edge of the protection umbrella region, wherein the contact hole is physically isolated from the gate region by the ILD layer, and wherein said creating the contact hole comprises (i) forming an oxide layer on the ILD layer, (ii) creating an opening in the oxide layer, and, (ii) etching the ILD layer through the opening using the oxide layer and the protection umbrella region as a blocking mask; and filling the contact hole with an electrically conducting material.
 13. The method of claim 12, wherein the protection umbrella region comprises silicon dioxide, and wherein the ILD layer comprises a low-K dielectric material, wherein K<3.5.
 14. The method of claim 12, wherein the electrically conducting material comprises tungsten.
 15. The method of claim 12, wherein said forming the protection umbrella region from the hard cap region comprises selectively depositing a dielectric material on only the hard cap region.
 16. A structure, comprising: (a) a semiconductor layer including (i) a channel region and (ii) first and second source/drain (S/D) regions, wherein the channel region is disposed between and electrically coupled to the first and second S/D regions; (b) a gate dielectric region in direction physical contact with the channel region via an interfacing surface which defines a reference direction perpendicular to the interfacing surface, wherein the gate dielectric region is above the channel region in the reference direction; (c) a gate region in direct physical contact with the gate dielectric region, wherein the gate dielectric region is sandwiched between and electrically insulates the gate region and the channel region; (d) a protection umbrella region on the gate region, wherein the protection umbrella region comprises a first dielectric material, and wherein the gate region is completely in a shadow of the protection umbrella region, wherein the shadow of the protection umbrella region comprises a space shielded by the protection umbrella region from an imaginary light point source (i) directly above the protection umbrella region in the reference direction and (ii) infinitely far from the protection umbrella region; and (e) a filled contact hole (i) directly above and electrically connected to the second S/D region and (ii) aligned with an edge of the protection umbrella region, wherein the contact hole is physically isolated from the gate region by an inter-level dielectric (ILD) layer, and wherein the ILD layer comprises a second dielectric material different from the first dielectric material.
 17. The structure of claim 16, wherein the first dielectric material comprises silicon dioxide, and wherein the second dielectric material comprises a low-K dielectric material, wherein K<3.5.
 18. The structure of claim 16, wherein the filled contact hole comprises tungsten.
 19. The structure of claim 16, wherein the gate region comprises (i) a polysilicon region on and in direct physical contact with the gate dielectric region and (ii) first and second gate silicide regions on first and second sidewalls of the polysilicon region, respectively.
 20. The structure of claim 19, wherein the first and second gate silicide regions are not in direct physical contact with the gate dielectric region. 